2014.06.08 Shanghai kai rich industrial co., LTD. (www.xfmjgy.cn) sales of P20 steel dies information: with the development of auto industry and the competition between industry, comprehensive mechanical properties and performance of automotive castings of the demand is higher and higher, so the high grade of as-cast nodular cast iron production application research, to improve product quality and competitiveness is of positive significance. This research embarks from the actual production, by controlling the casting of the chemical composition, improved breeds, especially the adjustment of alloying addition amount of Mn element, get the as-cast pearlite - existing body of the mixing matrix high grade of nodular cast iron, while reduce casting production cost, improve castings quality, and at the scene of the transit single tyre wheel production project. L in nodular cast iron manganese can hold up the decomposition of cementite and ferrite, because in the ductile iron manganese rarely combined with sulfur, and the main stabilizing effect of pearlite and carbide, can make the as-cast pearlite increases and refinement. Manganese can be solid soluble in ferrite, strengthening the role of the ferrite. Rich 2014.06.08 Shanghai kai industrial co., LTD. (sales P20 steel www.xfmjgy.cn) information: as a result, in the as-cast high grade of nodular cast iron pieces in production practice, the content of manganese is very important, general process control in the 0.4% to 0.6%, and is generally accepted that high manganese content in the ductile iron segregation is serious, can reduce the impact toughness of the casting. This research breakthrough tradition in the production of ductile iron on the limitations of manganese addition amount, the increase the content of manganese, obtain comprehensive mechanical properties conform to the requirements of as-cast high grade of nodular cast iron. 2.1 2 test results and analysis of test results for the amount of manganese changes the mechanical properties of ductile iron were investigated and the influence of the microstructure as shown in table l. Sample from table l Cll, C12, D11, manganese content increased from 0.48% to 1.2%, the strength from 473 mpa to 738 mpa, the hardness increased from HBl70 to I -- IB240, while elongation decreased from 21.86% to 21.86%. So in improving carbon, guarantee the spheroidizing, under the condition of more breeds, manganese content in o. 7 - o. 9% range to produce QT500-10, QT550-7, the manganese content in the 0.9-1.1% range to produce QT600.5, QT700.3. Table lMn addition amount of changes on the influence of mechanical properties. 2014.06.08上海偕富實(shí)業(yè)有限公司（銷售P20模具鋼www.xfmjgy.cn）的資訊：因此，在鑄態(tài)高牌號(hào)球墨鑄鐵件的生產(chǎn)實(shí)踐中，對(duì)錳的加入量控制顯得十分重要，一般工藝上控制在０．４％－０．６％，并普遍認(rèn)為過高的錳含量在球鐵中偏析嚴(yán)重，會(huì)降低鑄件的沖擊韌性。本研究突破傳統(tǒng)球鐵生產(chǎn)中對(duì)錳加入量的局限，采用提高錳加入量，獲得綜合機(jī)械性能符合要求的鑄態(tài)高牌號(hào)球墨鑄鐵。２試驗(yàn)結(jié)果與分析２．１試驗(yàn)結(jié)果錳加入量的變化對(duì)球鐵試樣力學(xué)性能和金相組織的影響如表ｌ所示。